Article title FRAGILE FRACTURE OF CYLINDRICAL SOLIDS UNDER NON-STATIONARY HEAT IMPACT
Authors V.A. Zhornik, P.A. Savochka
Section SECTION V. MODELING OF COMPLEX SYSTEMS
Month, Year 04, 2009 @en
Index UDC 539.4
DOI
Abstract Surface cracks’ propagation research in a heated cylinder made of inorganic glass under cooling in water is carried out. It is shown that under non-stationary temperature stresses a crack grows jump-like firstly and relatively slow after that not reaching the axis (the cylinder bursts). It was find out that the water besides cooling reveals itself as a surface active medium reducing glass strength. Comparison of glass heat resistance computational values with experimental data shown their good agreement was carried out.

Download PDF

Keywords Cylinder; inorganic glass; surface cracks; under cooling; water; temperature; experimental data.
References 1. Бартенев Г.М. Механические свойства и тепловая обработка стекла – М.: Госуд. изд-во литературы по строительству, архитектуре и строительным материалам, 1960. – 166 с.
2. Жорник А.И. Поля температур и напряжений, возникающие в твердых телах цилиндрической формы при тепловых нестационарных воздействиях // Диссертация канд. физ-мат. наук. – М.: МГПИ, 1972. – 201 с.
3. Tabata K., Moriya T. On the thermal endurance of glass // J. Amer. Ceram. Soc. 1934. V. 17, №2, P. 31-39.
4. Черепанов Г.П. Механика хрупкого разрушения. – М.: Наука, 1974. – 640 с.
5. Zhornik V.A., Prokopenko Yu.A., Rybinskaya A.A., Savochka P.A. Ring-shaped crack propagation in a cylinder under nonsteady cooling // High Performance Structures and Materials III. – WIT Press Southampton U.K., Boston USA, 2006, P. 521–526.
6. Андерсон О.Л. Критерий Гриффитса при разрушении стекла // Атомный механизм разрушения. Материалы Международной конференции по вопросам разрушения. Свомпскотт (США), 1959. – C. 331-353.
7. Бартенев Г.М. Сверхпрочные и высокопрочные неорганические стекла. – М.: Стройиздат, 1974. – 240 с.

Comments are closed.